Laboratory scale electroplating and processing of long lengths of in situ Cu-Nb₃Sn superconductors

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1016/0011-2275(84)90123-1
AuteurRechercher : 1; Rechercher : ; Rechercher : ; Rechercher :
Affiliation
  1. Conseil national de recherches Canada. Institut des matériaux industriels du CNRC
FormatTexte, Article
Résumé
The high temperature gradient solidification (HTGS) system for continuous casting of 12.7 mm diameter rods of in situ Cu-Nb is briefly reviewed. A laboratory scale continuous tin electroplating system is described and used to evaluate the effect of various parameters of the alkaline and acid baths plating process. Tin electroplating is shown to be simple and reliable. With an 8 m immersion length production speeds of ∼ 1 m min−1 are possible in an alkaline bath at 80°C. An acid bath gives satisfactory tinning deposits with a production speed of up to 3 m min−1 at room temperature.
Date de publication
Maison d’éditionElsevier
Dans
  • Cryogenics 24, nº 4 : 171–174.
Langueanglais
Publications évaluées par des pairsOui
Numéro du CNRCCNRC 21363
NRC-IGM-83-071-082
Numéro NPARC23003999
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrementcf4a4a62-a89a-4f45-ab1b-37daa9cab602
Enregistrement créé2018-09-13
Enregistrement modifié2020-03-13
Date de modification :