Hot corrosion degradation of a marine engine combustor liner

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1080/10426919508935078
AuteurRechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher :
Affiliation
  1. Conseil national de recherches du Canada. Institut de recherche aérospatiale du CNRC
FormatTexte, Article
Résumé
This paper summarizes the results of a failure investigation carried out on the combustor liner of a marine engine. Severe Type I hot corrosion attack was observed in the fuel swirler nozzle regions along the combustion side of the dome section. Degradation of the Hastelloy sheet metal parts in these regions led to burn throughs and cracking whereas the X-40 cast parti remained unaffected. Thermal fatigue cracking was also prevalent in the bulk of the Hastelloy dome section. These degradation mechanisms eventually led to the premature retirement of the combustor liner.
Date de publication
Maison d’éditionInforma UK Limited
Taylor and Francis Group
Dans
  • Materials and Manufacturing Processes 10, nº 5 (septembre 1995) : 887–901.
Langueanglais
Publications évaluées par des pairsOui
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrementc51dd586-7a1f-4762-8f0c-cc487bea98da
Enregistrement créé2023-10-03
Enregistrement modifié2023-10-03
Date de modification :