Compression of semisolid dendritic and non-dendritic Zn-Al alloys at low strain rates

Autre titre	Compression of semi-solid dendritic and non-dendritic Zn-Al alloys at low strain rates
DOI	Trouver le DOI : https://doi.org/10.1016/0025-5416(84)90063-6
Auteur	Rechercher : LeHuy, H.¹; Rechercher : Blain, J.¹; Rechercher : Bata, G. L.¹; Rechercher : Masounave, J.¹
Affiliation	Conseil national de recherches Canada
Format	Texte, Article
Résumé	The behaviour of semisolid Zn-Al alloys with a dendritic or a non-dendritic structure was studied in compression between two parallel plates. Small cylindrical specimens were deformed at constant strain rates ranging from 0.012 to 0.72 mm mm⁻¹ s⁻¹ and at various temperatures ranging from 350 to 443 °C. Dendritic specimens deformed with severe segregation and their structure broke down. Stir-cast specimens behaved more homogeneously. At 433 °C, their spheroid particle structure was preserved and the deformation strength was lower.
Date de publication	1984-11-01
Maison d’édition	Elsevier
Dans	Materials Science and Engineering 67, nº 2 : L29–L32.
Langue	anglais
Publications évaluées par des pairs	Oui
Numéro du CNRC	CNRC 23364 NRC-IGM84-205-136
Exporter la notice	Exporter en format RIS
Signaler une correction	Signaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement	af22de60-d441-4b2a-b411-7f05796036b8
Enregistrement créé	2019-03-26
Enregistrement modifié	2020-03-13

Détails de la page