The role of hot-working on the microstructure and mechanical properties of the L1₂-type manganese-modified Al₃Ti alloy

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1016/0921-5093(92)90222-M
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher :
FormatTexte, Article
ConférenceSecond International ASM Conference on High Temperature Aluminides and Intermetallics, September 16-19, 1991, San Diego, USA
Résumé
The crystal structure of a manganese-modified Al3Ti intermetallic alloy has been changed from the tetragonal D022 to the L12 cubic structure. The cast alloy shows considerable compression ductility at room temperature. To improve its mechanical properties further, hot-working experiments have been conducted. The results showed that the Al67Mn8Ti25 intermetallic alloy maintains very good hot-workability, the cast alloy can be reduced 60% by a single hot-pressing stroke without cracking. The role of hot-working on the microstructure and the mechanical properties of the alloy have been studied. It was found that the hot-worked alloy shows a deformed structure and some work-hardening after hot-working. Experiments indicated that the starting temperature for recrystallization is about 1173 K and complete recrystallization of the deformed alloy occurs at about 1273 K. Good hot-workability and a high recrystallization temperature permit potential for elevated temperature use. A transmission electron microscopy study on the evolution of dislocation structures in the recovery and recrystallization processes is also reported.
Date de publication
Maison d’éditionElsevier
Dans
  • Materials Science and Engineering: A 153, nº 1-2 (30 mai 1992) : 370–376.
Langueanglais
Publications évaluées par des pairsOui
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro NPARC21277140
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrementaf08140e-afae-4ad5-ba77-3ffe77a5ae07
Enregistrement créé2015-12-16
Enregistrement modifié2020-09-01
Date de modification :