3D Porous Fe/N/C spherical nanostructures as high-performance electrocatalysts for oxygen reduction in both alkaline and acidic media

Téléchargement
  1. (PDF, 2.1 Mio)
  2. (PDF, 1.3 Mio)
DOITrouver le DOI : https://doi.org/10.1021/acsami.7b12666
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher :
FormatTexte, Article
Sujet3D; Fe/N/C; nonprecious metal catalyst; oxygen reduction reaction; porous
Résumé
Exploring inexpensive and high-performance nonprecious metal catalysts (NPMCs) to replace the rare and expensive Pt-based catalyst for the oxygen reduction reaction (ORR) is crucial for future low-temperature fuel cell devices. Herein, we developed a new type of highly efficient 3D porous Fe/N/C electrocatalyst through a simple pyrolysis approach. Our systematic study revealed that the pyrolysis temperature, the surface area, and the Fe content in the catalysts largely affect the ORR performance of the Fe/N/C catalysts, and the optimized parameters have been identified. The optimized Fe/N/C catalyst, with an interconnected hollow and open structure, exhibits one of the highest ORR activity, stability and selectivity in both alkaline and acidic conditions. In 0.1 M KOH, compared to the commercial Pt/C catalyst, the 3D porous Fe/N/C catalyst exhibits ∼6 times better activity (e.g., 1.91 mA cm–2 for Fe/N/C vs 0.32 mA cm–2 for Pt/C, at 0.9 V) and excellent stability (e.g., no any decay for Fe/N/C vs 35 mV negative half-wave potential shift for Pt/C, after 10000 cycles test). In 0.5 M H2SO4, this catalyst also exhibits comparable activity and better stability comparing to Pt/C catalyst. More importantly, in both alkaline and acidic media (RRDE environment), the as-synthesized Fe/N/C catalyst shows much better stability and methanol tolerance than those of the state-of-the-art commercial Pt/C catalyst. All these make the 3D porous Fe/N/C nanostructure an excellent candidate for non-precious-metal ORR catalyst in metal–air batteries and fuel cells.
Date de publication
Maison d’éditionACS
Dans
  • ACS Applied Materials & Interfaces 9, nº 42 : 36944–36954.
Langueanglais
Publications évaluées par des pairsOui
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro NPARC23002485
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement9f231b92-4db5-41e5-a140-4212a5c621f9
Enregistrement créé2017-11-16
Enregistrement modifié2020-05-30

Détails de la page

Par :

Date de modification :