Mullite alumina particulate composites by infiltration processing : II, infiltration and characterization

DOI	Trouver le DOI : https://doi.org/10.1111/j.1151-2916.1990.tb04266.x
Auteur	Rechercher : Marple, Basil R.; Rechercher : Green, David J.
Format	Texte, Article
Résumé	Mullite/alumina composites were fabricated by infiltrating porous alumina preforms with a hydrolyzed ethyl silicate sol. Evidence is presented which suggests that initial infiltration occurred without complete filling of the porosity by the sol. Multiple infiltrations were used to increase the amount of SiO₂ introduced but led to blockage of the pores in the surface of the preform. Sintered bodies had concentration gradients, SiO₂ decreasing from the surface inward. Although mullite limited grain growth in alumina, in partially modified bodies large grains (>1 mm) with a preferred orientation were observed at the interface between the two zones
Date de publication	1990-12-31
Maison d’édition	Wiley
Dans	Journal of the American Ceramic Society 73, nº 12 : 3611–3616.
Langue	anglais
Publications évaluées par des pairs	Oui
Publication du CNRC	Cette publication n’est pas du CNRC Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.
Numéro du CNRC	CNRC 33349 NRC-IMI91AP-20200-1207G
Numéro NPARC	23004500
Exporter la notice	Exporter en format RIS
Signaler une correction	Signaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement	803a0d69-a872-4f8c-b696-3eabf48dfbed
Enregistrement créé	2018-11-09
Enregistrement modifié	2020-03-17

Détails de la page