Fatigue life prediction of welded joints using the effective stress intensity factor range

Par Conseil national de recherches du Canada

AuteurRechercher : 1; Rechercher : 1; Rechercher :
Affiliation
  1. Conseil national de recherches Canada
FormatTexte, Article
ConférenceThe Mechanism of Fracture : Proceedings of the fracture-mechanism program and related papers presented at the International Conference and Exposition on Fatigue, Corrosion Cracking, Fracture Mechanics, and Failure Analysis, 2-6 December 1985, Salt Lake City, Utah, USA
Résumé
Since the early 70's, LEFM concepts have been applied to welded joints and have provided a more reliable fatigue life prediction method. However, even today, very little information is available on the effects of nothch plasticity and welding residual stress for the practical problem of a crack propogating from the weld toe
Date de publication
Maison d’éditionAmerican Society for Metals
Dans
  • International Conference and Exposition on Fatigue, Corrosion Cracking, Fracture Mechanics, and Failure Analysis : 245–253.
Langueanglais
Publications évaluées par des pairsOui
Numéro du CNRCCNRC 25087
NRC-IGM86-203-254
Numéro NPARC23004866
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement55986807-8a53-4d86-8df4-d0a85d9f4314
Enregistrement créé2019-01-07
Enregistrement modifié2020-03-17
Date de modification :