Laser weldability of Zr-2.5Nb alloy to AISI 410 stainless steel with Ni filler

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1016/j.jmatprotec.2017.12.003
AuteurRechercher : 1; Rechercher : ; Rechercher : 1; Rechercher :
Affiliation du nom
  1. Conseil national de recherches du Canada. Automobile et les transports de surface
FormatTexte, Article
Sujetdissimilar metal joining; laser beam welding; Zr-2.5Nb; AISI 410 stainless steel; Ni interlayer
Résumé
The nickel interlayer improved the laser weldability of Zr-2.5Nb to AISI 410 stainless steel. The fusion zone contained a large amount of refined and tough dendritic γ-Ni(Fe, Cr) solid solution (182 ∼ 268 HV), while the brittle Zr(Fe, Cr)2 intermetallic compound (1171 ∼ 1460 HV), which was the main phase as the result of direct welding of Zr-2.5Nb to SS410 as well as the source responsible for the welding cracks, disappeared. Only limited quantities of Zr2(Ni, Fe), Zr7Ni10 (and/or Zr2Ni7) intermetallics were present mainly in the form of thin layers (less than 200 μm thick in total) near the fusion interface with Zr-2.5Nb. Those Zr-Ni based intermetallics showed relatively higher toughness and lower hardness (301 ∼ 497 HV) than the brittle Zr(Fe, Cr)2, which reduced the overall cracking sensitivity of the laser-weld.
Date de publication
Maison d’éditionElsevier
Dans
  • Journal of Materials Processing Technology 255 : 184–194.
Langueanglais
Publications évaluées par des pairsOui
Numéro NPARC23002769
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement5054fcfb-b4ae-4bd8-8965-5f7f0da0791c
Enregistrement créé2018-02-05
Enregistrement modifié2020-03-16
Signaler un problème ou une erreur sur cette page
Date de modification :