| Téléchargement | - Voir la version finale : High-performance porous 3D Ni skeleton electrodes for the oxygen evolution reaction (PDF, 11.1 Mio)
|
|---|
| DOI | Trouver le DOI : https://doi.org/10.1016/j.jmrt.2024.10.113 |
|---|
| Auteur | Rechercher : Abbasi, Somayyeh; Rechercher : Guerreiro, Bruno1; Rechercher : Martin, Manuel H.1; Rechercher : Gaudet, Julie; Rechercher : Fakourihassanabadi, Mohsen; Rechercher : Thorpe, Steven; Rechercher : Guay, Daniel |
|---|
| Affiliation | - Conseil national de recherches Canada. Automobile et les transports de surface
|
|---|
| Format | Texte, Article |
|---|
| Sujet | water splitting; oxygen evolution electrocatalyst; large-scale skeleton electrode; cold spray; shock-wave induced spray; leaching; superaerophobic |
|---|
| Résumé | A key component of green hydrogen production technologies is the fabrication of large-scale porous transport layer (PTL) for use in anion electrolyte membrane water electrolysers (AEMWEs). One strategy to achieve that goal is to manufacture Ni-based 3D electrode skeletons that can be further catalyzed to achieve high current densities at low overpotentials. In the present work, shock-wave induced spray (SWIS) and cold spray (CS) deposition techniques were used to prepare 20 cm² Ni-based electrode skeletons. In our experimental conditions, the porosity of coatings prepared using the SWIS deposition system and Ni powders with particle sizes D50 = 32 and 75 μm never exceeded 28%. Higher porosity could only be achieved using the CS deposition system and a spheroidal Ni–Al powder, whose particles consist of an aluminum core encapsulated in a nickel shell. After Al leaching in an alkaline solution, the resulting electrodes showed good mechanical and structural integrity with up to 41% porosity. The electrochemical active surface area of the most porous electrodes is a factor of 2100 larger than a polished Ni plate, and it has superaerophobic properties with a captive air bubble contact angle of 151°. During 1 h of electrolysis, the overpotential at 100 mA cm−2 of the most active leached Ni–Al cold spray deposited electrode was 330 mV, compared to 380 mV for a Ni foam electrode. |
|---|
| Date de publication | 2023-10-16 |
|---|
| Maison d’édition | Elsevier |
|---|
| Licence | |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 3b134408-8f3c-4049-af0b-6f4455159528 |
|---|
| Enregistrement créé | 2024-03-22 |
|---|
| Enregistrement modifié | 2025-04-08 |
|---|