Mass transfer in a ErBa₂Cu₃O₇ pellet partially melted in a thermal gradient

Par Conseil national de recherches du Canada

Autre titreMass transfer in a ErBa2Cu3O7 pellet partially melted in a thermal gradient
DOITrouver le DOI : https://doi.org/10.1016/0167-577X(92)90002-2
AuteurRechercher : 1; Rechercher : 1; Rechercher : 1; Rechercher : 1
Affiliation
  1. Conseil national de recherches Canada. Institut des matériaux industriels du CNRC
FormatTexte, Article
Résumé
Melt texturing in high thermal gradients promotes the crystallization of oriented RBa₂Cu₃Oₓ grains which improves the critical current densities. However, the presence of high thermal gradients induces a transport of material that modifies the composition of the melt and disrupts the crystallization process. In this study, material transfer phenomena have been examined by crystallizing a ErBa₂Cu₃Oₓ pellet in a static thermal field. The influence of material transfer on the microstructure of textured pellets has been studied. These microstructures indicate that the material is transferred mainly by thermocapillarity. We also determined that the temperature of the characteristic ridge formed during crystallization was about 892 ± 10°C which corresponds closely to the solidification of the binary and ternary eutectic temperatures.
Date de publication
Maison d’éditionElsevier
Dans
  • Materials Letters 15, nº 1-2 : 1–7.
Langueanglais
Publications évaluées par des pairsOui
Numéro du CNRCCNRC 33756
NRC-IMI92AP-23500-1317-G
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement342301f4-c466-4643-bffc-c0b0d163d80b
Enregistrement créé2020-06-08
Enregistrement modifié2020-06-08
Date de modification :