Rheology of PVC. Part 5 : melt elasticity

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1002/vnl.730080405
AuteurRechercher : 1
Affiliation
  1. Conseil national de recherches Canada
FormatTexte, Article
Résumé
The behavior of PVC changes drastically with the temperature and the method of sample preparation. In the steady‐state shear mode, upon a decrease of the rate of deformation, the data may show either a steady increase of the shear viscosity or a leveling off to a Newtonian plateau. In the dynamic test mode, both the storage modulus, G′, and the loss modulus, G″, show an effect of the yield stress. Only at temperatures above 210°C are flow curves normal for polymer melts obtained. Rigid and nonrigid PVC formulations have been tested in Weissenberg Rheogoniometer, using steady‐state or dynamic test modes at temperatures from 140 to 220°C. It was observed that yield affects elasticity more (measured by the first normal stress difference or the storage modulus) than viscosity (expressed by the shear stress or the loss modulus). The corrected for yield plots of elastic vs. viscous parameter can be easily interpreted in terms of a composite flow.
Date de publication
Maison d’éditionWiley
Dans
  • Journal of Vinyl and Additive Technology 8, nº 4 : 156–159.
Langueanglais
Publications évaluées par des pairsOui
Numéro du CNRCCNRC 25399
NRC-IGM86-502-270
Numéro NPARC23004045
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement32cd4a61-9a0d-4ef0-8387-14a119bbbb64
Enregistrement créé2018-09-19
Enregistrement modifié2020-03-17
Date de modification :