Effect of Al content on the low-stress abrasive wear behaviour of Fe-18Mn-xAl-0.7C alloys

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1016/j.triboint.2023.108286
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher : ; Rechercher : 1Identifiant ORCID : https://orcid.org/0000-0002-7714-2061
Affiliation
  1. Conseil national de recherches Canada. Énergie, les mines et l'environnement
FormatTexte, Article
SujetFe-Mn-Al-C steels; abrasive wear; strain hardening mechanisms; stacking fault energy
Résumé
The low-stress ASTM-G65 abrasive wear behaviour was studied in a system of high manganese steels Fe-18Mn-xAl-0.7C with aluminium contents of 0%, 3%, 6% and 9.5% by weight and the results were compared with those of AISI D2 and AISI 9260 steels. By a completely randomized design (CRD), it was determined that the highest wear resistance corresponds to AISI D2 steel, followed by Fe18Mn0Al, Fe18Mn3Al, Fe18Mn9Al, Fe18Mn6Al and AISI 9260 steel. Using micro hardness tests, surface analysis and staking fault energy calculations it was possible to establish a relationship between wear resistance and the strain hardening mechanisms such as transformation induced plasticity (TRIP), twinning induced plasticity (TWIP) and microband induced plasticity (MBIP) for the Fe-Mn-Al-C steels under study.
Date de publication
Maison d’éditionElsevier
Dans
  • Tribology International 180, nº C, 108286 (23 janvier 2023) : 1–11.
Langueanglais
Publications évaluées par des pairsOui
Numéro du CNRCNRC-EME-56379
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement0d79ecd9-0f57-4085-8bed-6d40bad9b9e2
Enregistrement créé2023-03-20
Enregistrement modifié2023-03-21
Date de modification :