Residual stress in alumina-mullite composites

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1111/j.1151-2916.1991.tb04063.x
AuteurRechercher : ; Rechercher : ; Rechercher :
ÉditeurRechercher : Green, D. J.
FormatTexte, Article
Résumé
Lattice strains have been measured by neutron diffraction from the alumina matrix in alumina–mullite composite cylinders. Infiltration processing results in a macroscopic variation of mullite concentration and residual stress throughout the samples. At the midheight of the cylinder, the stress component parallel to the cylinder axis is in a compression of −130 ± 30 MPa with respect to the value near the top surface. At the surfaces, the stress component parallel to the surface is in a compression of −130 ± 30 MPa with respect to values near the midheight of the cylinder. An overall tensile shift of the macroscopic stress profile in a fully infiltrated specimen is interpreted as a grain interaction effect between the alumina and mullite constituents. The positional dependence of the mullite phase concentration is also determined by neutron diffraction
Date de publication
Maison d’éditionWiley
Dans
  • Journal of the American Ceramic Society 74, nº 3 : 579–583.
Langueanglais
Publications évaluées par des pairsOui
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro du CNRCCNRC 33347
NRC-IMI91AP-20200-1171-G
Numéro NPARC23004512
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement02e39984-371c-4758-905b-fd833593ba04
Enregistrement créé2018-11-09
Enregistrement modifié2020-03-17
Date de modification :