Gas solubility in and foamability of various forms of syndiotactic-polystyrene

From National Research Council Canada

DOIResolve DOI: https://doi.org/10.1177/026248930102000401
AuthorSearch for: ; Search for: ; Search for: ; Search for:
FormatText, Article
Abstract
A high pressure microbalance was used to measure solubility of CO₂ at 35°C and pressures to 55 atm in amorphous, meso, and α-crystalline forms of syndiotactic polystyrene, sPS. Diffusion coefficient of CO₂ in the various samples were derived from sorption kinetics. When normalized with respect to 100% amorphous content, the solubility and diffusivity of CO₂ was found to be highest in the semi-crystalline α-form, followed by the meso and the amorphous forms. This rather unusual observation was attributed to the existence of microvoids in α-sPS and meso-sPS, and due to the finite solubility of gas in the rigid amorphous phase associated with these two forms. All three forms of sPS were foamed at various temperatures in the range 50 to 295°C to give microcellular structures. The cell walls in foams obtained from amorphous sPS showed unusual, starburst type structure. The density of meso-sPS foams first decreased and then increased with foaming temperature due to the transformation of the mesophase to the α-phase with increasing temperature. The microvoids in α-sPS and meso-sPS are conjectured to serve as the nucleating sites rather than the often suggested phenomenon of heterogeneous nucleation induced by the crystallites.
Publication date
PublisherSage
In
  • Cellular Polymers 20, no. 4: 241–253.
Peer reviewedYes
NRC publication
This is a non-NRC publication

"Non-NRC publications" are publications authored by NRC employees prior to their employment by NRC.

NPARC number12744494
Export citationExport as RIS
Report a correctionReport a correction (opens in a new tab)
Record identifiera0b88b66-d3a4-4992-8f49-c6349307c0d0
Record created2009-10-27
Record modified2020-05-03
Date modified: