| DOI | Resolve DOI: https://doi.org/10.1016/0038-1098(94)00777-2 |
|---|
| Author | Search for: Siegele, R.; Search for: Haugen, H. K.; Search for: Lockwood, D. J.1; Search for: Bryskiewicz, B.1; Search for: Forster, J. S.; Search for: Andrews, H. R. |
|---|
| Affiliation | - National Research Council Canada. NRC Institute for Microstructural Sciences
|
|---|
| Format | Text, Article |
|---|
| Subject | A. nanostructures; A. semiconductors; D. optical properties; E. ion impact |
|---|
| Abstract | Samples of porous Si (PS) were prepared from p-type 10-35 [Omega]-cm Si under anodisation in aqueous HF (20%) for 10 min. The composition of the PS was measured by heavy-ion elastic recoil detection analysis (HIERDA). In all samples a considerable carbon content varying from 2-20% was measured, while the oxygen and hydrogen concentrations ranged from 2-25% and 10-25%, respectively. The sample wax removing procedure was identified as a source for the high carbon content. The concentration of carbon and its influence on the photoluminescence due to different treatments of PS was investigated. |
|---|
| Publication date | 1995-03 |
|---|
| In | |
|---|
| Language | English |
|---|
| NPARC number | 12333664 |
|---|
| Export citation | Export as RIS |
|---|
| Report a correction | Report a correction (opens in a new tab) |
|---|
| Record identifier | 43b5122a-8cbe-48b6-b74a-dc86494266d8 |
|---|
| Record created | 2009-09-10 |
|---|
| Record modified | 2020-04-29 |
|---|