Validation of the VUV-reflective coating for next-generation liquid xenon detectors

From National Research Council Canada

DOIResolve DOI: https://doi.org/10.1088/1748-0221/19/06/P06008
AuthorSearch for: ; Search for: ; Search for: ; Search for: 1ORCID identifier: https://orcid.org/0000-0003-4403-8214; Search for:
Affiliation
  1. National Research Council of Canada. Quantum and Nanotechnologies
FormatText, Article
Subjectvacuum ultraviolet; xenon detector; diffuse reflectance; dark matter detectors (WIMP, axions, etc.); double-beta decay detectors; noble liquid detectors (scintillation, ionization, double-phase)
Abstract
Coating detector materials with films highly reflective in the vacuum ultraviolet region improves sensitivity of the next-generation rare-event detectors that use liquid xenon. In this work, we investigate the MgF₂-Al-MgF₂ coating designed to achieve high reflectance at 175 nm, the mean wavelength of liquid xenon (LXe) scintillation. The coating was applied to an unpolished, passivated copper substrate mimicking a realistic detector component of the proposed nEXO experiment, as well as to two unpassivated substrates with “high” and “average” levels of polishing. After confirming the composition and morphology of the thin-film coating using TEM and EDS, the samples underwent reflectance measurements in LXe and gaseous nitrogen (GN2). Measurements in LXe exposed the coated samples to -100°C for several hours. No peeling of the coatings was observed after several thermal cycles. Polishing is found to strongly correlate with the measured specular reflectance (Rspec). In particular, 5.8(5)% specular spike reflectance in LXe was measured for the realistic sample at 20° of incidence, while the values for similar angles of incidence on the high and average polish samples are 62.3(1.3)% and 27.4(7)%, respectively. At large angles (66°–75°), the Rspec in LXe for the three samples increases to 23(5)%, 80(8)%, and 84(18)%, respectively. The  Rspec at around 45° was measured in both GN2 and LXe for average polish sample and shows a reasonable agreement. Importantly, the total reflectance of the samples is comparable and estimated to be 92(8)%, 85(8)%, and 83(8)% in GN2 for the realistic, average, and high polish samples, respectively. This is considered satisfactory for the next-generation LXe experiments that could benefit from using reflective films, such as nEXO and DARWIN, thus validating the design of the coating.
Publication date
PublisherIOP Publishing
Sissa Medialab
In
  • Journal of Instrumentation 19, no. 06, P06008 (6 June 2024): 1–17.
Other version
  • Bajpai, D., A. Best, I. Ostrovskiy, D. Poitras, and W. Wang. ‘Validation of the VUV-Reflective Coating for next-Generation Liquid Xenon Detectors’. ArXiv, 2024. https://doi.org/10.48550/ARXIV.2402.15177.
LanguageEnglish
Peer reviewedYes
Export citationExport as RIS
Report a correctionReport a correction (opens in a new tab)
Record identifier34724f95-ed2a-4381-b945-9f27d265a8ad
Record created2024-10-28
Record modified2024-10-29
Date modified: